We'd say the key is for something to be Stress Relieved and from a practical standpoint it does not matter if something was cryo or heat-based. The key is to reset the grain structure of the metal to ensure that as it heats up from firing the hoop stress does not cause the barrel to move.
The earlier PSL statement we would have immediately called out the barrel not being stress relieved.